Sahil Metals stands out as a top manufacturer and supplier in Riyadh, Saudi Arabia, specializing in high-quality Stainless Steel 416 Bars and Rods tailored to meet a variety of industrial needs. Known for their precision, durability, and a strong commitment to customer service, Sahil Metals guarantees that every product meets international quality and performance standards. The Stainless Steel 416 Bars and Rods are celebrated for their excellent machinability, decent corrosion resistance, and impressive strength. They find applications in sectors like construction, petrochemical, automotive, and mechanical industries, where Sahil Metals delivers reliable, cost-effective solutions with prompt delivery and consistent quality.
These bars and rods are martensitic stainless steels that contain 12–14% chromium, with added sulfur to boost machinability. They also have small amounts of manganese, silicon, and phosphorus, which enhance their overall performance. With a tensile strength ranging from 550–700 MPa, they exhibit good hardness and toughness after heat treatment. While their corrosion resistance is moderate compared to austenitic grades, they excel in machinability, making them the top choice among all stainless steels. Additionally, Stainless Steel 416 Bars and Rods are magnetic and can be hardened for demanding engineering tasks.
Specification : ASTM A276, A479 / ASME SA276, SA479
Standard : EN, DIN, JIS, ASTM, BS, ASME, AISI
Round Bars : Outside Diameter in the range of 4mm to 500mm
Bright Bars : Outside Diameter in the range of 4mm to 100mm
Hex Bars : 18mm – 57mm (11/16″ to 2-3/4″)
Square Bars : 18mm – 47mm (11/16″ to 1-3/4″)
Finish : Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish
Length : 1 to 6 Meters, Custom Cut Lengths
Form : Round, Square, Hex (A/F), Rectangle Etc.
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
| SS 416 | 0.15 max | 1.25 max | 1.0 max | 0.06 max | 0.15 min | 14.00 – 12.00 | 0.6 | – | – |
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 8.0 g/cm3 | 1454 °C (2650 °F) | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 35 % |
| STANDARD | WERKSTOFF NR. | UNS | JIS | EN | BS |
| SS 416 | 1.4005 | S41600 | SUS 416 | X12CrS13 | 416S21 |
Stainless Steel 416 is a martensitic stainless steel with a higher level of sulfur and carbon content, which enhances its machinability compared to other stainless steels. This alloy offers improved strength and hardness while still maintaining a good level of corrosion resistance, making it suitable for precision machining.
Yes, Stainless Steel 416 can be heat-treated to increase its hardness. It can be hardened through a quenching and tempering process, which improves its strength, making it ideal for applications that require high wear resistance.
Industries that require precision components with great machinability and sufficient corrosion resistance widely use Stainless Steel 416 Bars and Rods. They’re commonly found in the production of shafts, gears, fasteners, screws, valves, and pump parts. Their versatility in being machined into complex shapes makes them perfect for automotive, mechanical, and general engineering applications. Moreover, these bars and rods are utilized in construction and industrial equipment where strength, cost-effectiveness, and reliability are essential. Their performance in moderately corrosive environments ensures they provide long-lasting and efficient service.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Sahil Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Riyadh, Saudi Arabia