Sahil Metals is a leading manufacturer and supplier based in Riyadh, Saudi Arabia, specializing in quality steel products for a range of industries. Committed to providing excellent products and customer satisfaction, we offer a comprehensive range of Hastelloy W Bars and Rods, known for exceptional corrosion resistance, high strength and durability in internal environments is strong. These high-quality materials are widely used in chemical manufacturing, aerospace, and other high-efficiency industries. At Sahil Metals, we ensure that every Hastelloy W Bar and Rod meets the highest industry standards, providing reliable solutions to our customer’s demanding needs.
Hastelloy W Bars and Rods are primarily made up of nickel (about 65%), with notable amounts of molybdenum (around 28%), iron (5%), and cobalt (up to 2.5%). This alloy is particularly known for its outstanding weldability, especially in thicker joints, and it resists cracking even under intense heat. It has a tensile strength ranging from 690 to 790 MPa, a yield strength between 275 and 350 MPa, and good elongation properties. Hastelloy W maintains its structural integrity in high-temperature settings and during thermal cycling, making it perfect for demanding fabrication processes that require reliable mechanical performance.
| Standards : | AMS 5755, AMS 5786, AWS A5.14 & ASME SFA 5.14 |
| Dimensions : | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Wire : | Thickness starting from 0.05mm |
| Round bar size : | Diameter: 3-~800mm |
| Hex Bar size : | 2-100mm A/F |
| Flat bar size : | Thickness: 2 -100mm / Width: 10 to 500mm |
| Square bar size : | 4 to 100mm |
| Rectangular Bars Size : | 33 x 30mm to 295 x 1066mm |
| Hollow Bar : | 32mm OD x 16mm ID to 250mm OD x 200mm ID |
| Tolerance : | H8, H9, H10, H11, H12, H13K9, K10, K11, K12 or as per clients’ requirements |
| Finish : | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| C | Mn | Si | S | Co | Ni | Cr | Fe | Mo | P | Cu |
| 0.12 | 1.0 | 1.0 | 0.03 | ≤2.5 | – | 4.0-6.0 | 4.00 – 7.00 | 23-26 | 0.04 | ≤0.5 |
| Yield strength (MPa) | Tensile strength(MPa) | Impact test | Elongation (%) | Reduction in cross section on fracture (%) | As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 765 (≥) | 352 (≥) | 31 | 24 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 214 |
| STANDARD | WERKSTOFF NR. | UNS |
| Hastelloy W | – | N10004 |
Hastelloy W Bars offer exceptional resistance to corrosion, especially in harsh chemical environments, along with high strength and excellent weldability. They are ideal for high-temperature applications due to their thermal stability.
Yes, Hastelloy W rods can be welded. They are known for their excellent weldability, making them suitable for high-temperature and corrosive environments.
Hastelloy W rods are available in a range of diameters, typically from 1/8 inch to several inches, and can be supplied in various finishes, including mill, polished, and ground. Custom sizes and finishes can also be provided based on specific requirements.
These Hastelloy W Bars and Rods find extensive use in aerospace, nuclear power systems, and chemical processing equipment, particularly where high weld integrity is essential. They are perfect for creating components like pressure vessels, piping systems, and structural parts that face extreme heat or corrosive conditions. The alloy’s superb weldability and resistance to cracking during welding make it especially valuable for thick, high-stress joints. Its ability to endure high temperatures and mechanical stress makes Hastelloy W a preferred choice for mission-critical applications in challenging industrial environments.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Sahil Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Riyadh, Saudi Arabia