Sahil Metals, located in Riyadh, Saudi Arabia, stands out as a top manufacturer and supplier of premium **Tool and Die Steel A2 Bars**. These A2 steel bars are celebrated for their remarkable blend of toughness and wear resistance, making them a go-to choice for precision tooling applications. At Sahil Metals, we pride ourselves on delivering materials that adhere to international quality standards, ensuring that our products are durable and reliable for even the most demanding industrial tasks. With a strong emphasis on precision manufacturing and prompt delivery, we have become a trusted partner for customers throughout Saudi Arabia and the Middle East who are in search of dependable tool steel solutions.
A2 Tool and Die Steel Bars are air-hardening, medium-alloy tool steels that typically contain around 1.0% carbon, 5.0% chromium, 1.0% molybdenum, and 1.0% vanadium. This specific composition results in high hardness, impressive wear resistance, and outstanding toughness. After heat treatment, A2 steel can reach hardness levels between 57-62 HRC, offering good dimensional stability and resistance to deformation. Its air-hardening characteristic helps reduce distortion during heat treatment, making it perfect for intricate and precise tooling applications that demand consistent performance.
| ASTM A681 | C | Mn | P | S | Si | Cr | V | Mo | ||||||
| A2/T30102 | 0.95 | 1.05 | 0.40 | 1.00 | 0.03 | 0.03 | 0.10 | 0.50 | 4.75 | 5.50 | 0.15 | 0.50 | 0.90 | 1.40 |
| DIN ISO 4957 | C | Mn | P | S | Si | Cr | V | Mo | ||||||
| 1.2363/X100CrMoV5 | 0.95 | 1.05 | 0.40 | 0.80 | 0.03 | 0.03 | 0.10 | 0.40 | 4.80 | 5.50 | 0.15 | 0.35 | 0.90 | 1.20 |
| JIS G4404 | C | Mn | P | S | Si | Cr | V | Mo | ||||||
| SKD12 | 0.95 | 1.05 | 0.40 | 0.80 | 0.03 | 0.03 | 0.10 | 0.40 | 4.80 | 5.50 | 0.15 | 0.35 | 0.90 | 1.20 |
| BS 4659 | C | Mn | P | S | Si | Cr | V | Mo | ||||||
| BA2 | 0.95 | 1.05 | 0.30 | 0.70 | 0.035 | 0.035 | . . . | 0.40 | 4.75 | 5.25 | 0.15 | 0.40 | 0.90 | 1.10 |
| Properties | Metric | Imperial |
| Hardness, Rockwell C (as air-hardened (63-65 HRC average), 60-62 HRC at 205°C, 59-61 HRC at 260°C, 58-60 HRC at 315°C, 57-59 HRC at 370°C and 425°C and 480°C, 56-58 HRC at 540°C, 50-52 HRC at 595°C, 42-44 HRC at 650°C) | 64 | 64 |
| Bulk modulus (typical for steels) | 140 GPa | 20300 ksi |
| Machinability (based on carbon tool steel) | 65% | 65% |
| Shear modulus | 78.0 GPa | 11300 ksi |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Elastic modulus | 190-210 GPa | 27557-30457 ksi |
| Country | USA | German | Japan | British |
| Standard | ASTM A681 | DIN EN ISO 4957 | JIS G4404 | BS 4659 |
| Grades | A2/T30102 | 1.2363/X100CrMoV5 | SKD12 | BA2 |
| Properties | Conditions | ||
|---|---|---|---|
| T (°C) | Treatment | ||
| Thermal expansion | 10.7 x 10-6/ºC | 20-100 | – |
The standard annealing temperature for A2 tool and die steel bars is typically between 800°C to 850°C (1472°F to 1562°F), followed by slow cooling to relieve internal stresses and soften the material.
A2 tool and die steel bars resist corrosion through their high chromium content, forming a protective oxide layer that enhances resistance to rust and wear, especially in cold-work applications.
A2 Tool Steel Bars find their place in the manufacturing of dies, punches, blanking tools, and shear blades, where a mix of toughness and wear resistance is crucial. They excel in cold work applications that face high impact and abrasion. Industries such as automotive, metal stamping, and fabrication often depend on A2 steel for tools that require a long service life and resistance to chipping or cracking. Its versatility and durability make it a favored option for a wide array of tooling needs.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.